Molding sand is a fine-grained mineral mixture that is permeated with an...
Phosphorus copper cartridge used to deoxidize and fluidify the bronze...
Manufacturers
No manufacturer
Suppliers
No supplier
Molding sand is a fine-grained mineral mixture that is permeated with an oily binder. For metal with 0% iron, like bronze, brass, aluminium
Phosphorus copper cartridge used to deoxidize and fluidify the bronze molten bath. It causes a rise in temperature. Add at the last minute, before pouring, when everything is melted. Foam after putting in the cartridge.1 piece for 50kg brons
Refractory plaster to cast bronze, brass, glass Ratio water/plaster = 27/100plaster/water= 380/100
Silicone rubber similar of DC3481, to use with Curing agent W22.Ratio silicone/curing agent= 100/5 (demold after 24h). You can use thixo DC to make it thicker
Curing agent for silicone W22Ratio curing agent/silicone: 5/100Demold after 24h
Alginate is a natural material for the making of very precise prints of objects. Completely harmless: can be used on the body.Cured in 3-5 minutes at 20°C.Mixing rate 100 gr powder + 200 ml water or 100 gr powder + 200 ml water
Ratio silicone/catalyst DC 81= 100/53 catalysts available: 81R (24h), 81 fast (1h30), 81 VF (few minutes)To thicken: agent thixotrope Dow CorningCan by used with filler
Cut the desired length of the Plaster of Paris. Let it soak in water during 10-15 seconds, after which the plaster becomes moldable and self-adhesive. Sticks on itself, on skin and all other materials. Cures after 8 minutes.
Silicon-Carborandum Crucible (SIC) Crucible for non-ferrous metals, such as bronze, brass, aluminum, ... Maximum operating temperature 1200-1250 ° C